Double Side Polished Co2+:MgAl2O4 Single Crystal Substrate
Co2+:MgAl2O4 is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths.
High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
● Suitable for 1.54μm eye-safe lasers
● High absorption section and no excited state absorption
Co2+:MgAl2O4 Single Crystal Substrate Main Properties:
| Specifications |
| Material |
Co2+:MgAl2O4 |
| Orentation |
<111>+/-0.5° |
| Doping rate of Co2+ |
0.05-0.3 atm% |
| Optical density |
0.1-0.9 |
| Absorption coefficient |
1.0cm-1-7cm-1 |
| Transmittance |
30%-99% |
| Absorption section |
3.5 x 10-19cm2 |
| Thickness/Diameter tolerance |
+/-0.1mm |
| Parallelism |
10″ |
| Perpendicular |
5′ |
| Surface quality |
10/5 |
| Wavefront distortion |
Lambda/8 @ 632nm |
| Flatness |
Lambda/8 @ 632nm |
| Aperture |
>90% |
| Chamfer |
0.1 x 45° |
| HR Coating |
<=0.2%(@ 1533nm) |
| Damage threshold |
>500MW/cm2 |
Co2+:MgAl2O4 Single Crystal Substrate Applications
- Eye-safe 1540 nm Er:glass laser
- 1440 nm laser
- 1340 nm laser
- Eye-safe laser range finder
Co2+:MgAl2O4 Single Crystal Substrate Brief Introduction:
- Co2+:MgAl2O4 (Co2+:Spinel or Co:MALO) crystals is a new material for passive Q-switching in lasers emitting from 1.2 to 1.6 µm, in particular, for eye-safe 1.54 µm Er:glass laser, but also works at 1.44 µm and 1.34 µm wavelengths.
- High absorption cross section (3.5 × 10-19cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping.
- Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
- We offer the high quality Co:Spinel crystals materials with high optical quality and uniform distribution of Co2+ in laser grade polishing and coatings.
Co2+:MgAl2O4 Feature:
- Suitable for 1540 nm eye-safe lasers
- High absorption section
- Negligible excited state absorptio
- High optical quality
- Uniformly distributed Co
About US
Crystro has perfect automatic production equipment, the current products are mainly concentrated in the YAG, TGG, TSAG,GGG, LGS, Ce:GAGG , Ce:YAG andCe: LuYAG production. the application of advanced process technology of manufacturing, reducing energy consumption to ensure sustainable development field of research and development.